ukuhlanzeka okuphezulu kwe-graphite induku
I-Hebei Hexi Carbon Co., LTD.Umkhiqizo we-graphite rod wokuhlanzeka okuphezulu kwethebula lenkomba yenkomba yamakhemikhali.
| Izimoto ezintsha zamandla, ukusakaza okuqhubekayo nezinye izimboni ezisetshenziswa ekusebenzeni kwezinto ezibunjiwe ze-graphite | ||||||||||
| Ibhrendi | Ukuminyana | Ukumelana nogesi | I-Conductivity yokushisa | I-coefficient yokwanda okushisayo (izinga lokushisa legumbi -600 ℃) | Ukuqina koShore | Amandla e-Flexural | Amandla acindezelayo | I-modulus ye-elasticity | umlotha | Okuqukethwe komlotha okuhlanziwe |
| g/cm3 | µΩm | W/mk | 10-6/℃ | I-HSD | Mpa | Mpa | I-Gpa | I-PPM | I-PPM | |
| I-HX-5 | 1.80 | 8~10 | 125 | 4.9 | 45 | 40 | 80 | 9.5 | 500 | 50 |
| Ukucaciswa kokusebenza kwezinto ze-graphite ezicindezelwe yi-isostatic zokushisa okuphezulu kanye nemboni ye-hydrogen fuel cell bipolar plate | ||||||||||
| Ibhrendi | Ukuminyana | Ukumelana nogesi | I-Conductivity yokushisa | I-coefficient yokwanda okushisayo (izinga lokushisa legumbi -600 ℃) | Ukuqina koShore | Amandla e-Flexural | Amandla acindezelayo | I-modulus ye-elasticity | umlotha | Okuqukethwe komlotha okuhlanziwe |
| g/cm3 | µΩm | W/mk | 10-6/℃ | I-HSD | Mpa | Mpa | I-Gpa | I-PPM | I-PPM | |
| I-HX-5P | 1.90 | 8~10 | 135 | 3.6 | 55 | 55 | 105 | 12 | 500 | 50 |
| Inkomba yokusebenza ye-isostatic ecindezelwe izinto zegraphite yemboni ye-photovoltaic | ||||||||||
| Ibhrendi | Ukuminyana | Ukumelana nogesi | I-Conductivity yokushisa | I-coefficient yokwanda okushisayo (izinga lokushisa legumbi -600 ℃) | Ukuqina koShore | Amandla e-Flexural | Amandla acindezelayo | I-modulus ye-elasticity | umlotha | Okuqukethwe komlotha okuhlanziwe |
| g/cm3 | µΩm | W/mk | 10-6/℃ | I-HSD | Mpa | Mpa | I-Gpa | I-PPM | I-PPM | |
| I-HX-4 | 1.72 | 10~13 | 100 | 5 | 40 | 30 | 65 | 9.2 | 500 | 50 |
| I-HX-6 | 1.81 | 11-14 | 120 | 4.5 | 60 | 45 | 90 | 10.5 | 500 | 50 |
| Izakhiwo zezinto ze-graphite ezicindezelwe ze-isostatic ezisetshenziswa embonini ye-EDM | ||||||||||
| Ibhrendi | Ukuminyana | Ukumelana nogesi | Ukuqina kogu | Ukuqina kwe-Rockwell | Amandla e-Flexural | Usayizi wokusanhlamvu omaphakathi | ||||
| g/cm3 | µΩm | I-HSD | HRL | Mpa | μm | |||||
| I-KYX-7 | 1.76 | 12-16 | 40 | 94 | 40 | 8 | ||||
| I-KYX-60 | 1.78 | 12-16 | 45 | 100 | 45 | 4 | ||||
| I-KYD-8 | 1.84 | 12-16 | 70 | 105 | 55 | 6 | ||||
| Ingilazi egobayo eshisayo ye-3D nezinye izimboni ezinezinkomba zokusebenza kwe-graphite ecindezelwe yi-isostatic | |||||||||
| Ibhrendi | Ukuminyana | Ukumelana nogesi | I-Conductivity yokushisa | I-coefficient yokwanda okushisayo (izinga lokushisa legumbi -600 ℃) | Ukuqina koShore | Amandla e-Flexural | Amandla acindezelayo | I-modulus ye-elasticity | Usayizi wokusanhlamvu omaphakathi |
| g/cm3 | µΩm | W/mk | 10-6/℃ | I-HSD | Mpa | Mpa | I-Gpa | μm | |
| I-KYD-9 | 1.88-1.92 | 10~14 | 110 | 3.9 | 75 | 60 | 125 | 12 | 2 |
| I-KYD-30 | 1.81 | 15-19 | 80 | 5.8 | 80 | 43 | 130 | 7.5 | 12 |
| I-KYX-700 | 1.85 | 12-16 | 105 | 4 | 55 | 50 | 105 | 10 | 8 |
| I-KYX-60S | 1.85 | 12-16 | 110 | 4 | 60 | 55 | 120 | 11 | 4 |
 |  |  |